To examine the effect of heat treatment temperature in finishing process on PET/PBT Fabric, PET/PBT Fabrics were treated at different relaxing temp., pre-set temp., and final-set temp.. The dimensions such as thickness and density were measured, and the handles were evaluated by Kawabata system. In relaxing which was wet heat treatment, thickness and bulkiness were increased, and NUMERI, FUKURAMI, SOFUTOSA, and THV also were increased but KOSHI was decreased with elevating temperature. With elevating pre-set temp., thickness and bulkiness were decreased, but KOSHI was increased. NUMERI, FUKURAMI, SOFUTOSA, and THV were the best at 180$^{circ}C$ pre-set treatment. In final-set which was dry heat treatment like pre-set, thickness, bulkiness, NUMERI, HUKURAMI, SOFUTOSA, and THV were decreased, but KOSHI value was increased with elevating temperature. Therefore the best heat treatment condition was 130$^{circ}C$ relaxing, 180$^{circ}C$ pre-set, and 160$^{circ}C$ final-set. And the handle of PET/PBT Fabric was affected much more by relaxing temp. than pre-set temp. and final-set temp.