BaZr $O_3$-based proton conductors in which B-site cations are partially substituted by Ce and Yb were fabricated by a solid state reaction method. The electrical properties of the specimens were measured by using impedance analyzer in dry air and wet air atmospheres. The electrical conductivity showed higher value in wet air than in dry air at below $600^{circ}C$. As the Ce content increased, the electrical conductivity increased. Among four compositions, BaZ $r_{0.8}$C $e_{0.15}$Y $b_{0.05}$ $O_3$$_{-{delta}}$ specimen showed the highest electrical conductivity,1.72$ imes$10$^{-3}$ S$cm^{-1}$ /, at 80$0^{circ}C$. In the low temperature region, the electrical conductivity was higher in wet air than in dry air. However, as the temperature increased, the proton conductivity reduced and thus the electrical conductivity showed similar value at approximately $700^{circ}C$.>.>.>.