Ti - Si - N hard films were deposited on SKD11 steel substrates by a hybrid deposition system, where TiN was deposited by AIP method while Si was incorporated by sputtering one. The microstructure of Ti-Si-N films was revealed to be a composite of TiN crystallites and amorphous Si3N4 by instrumental analyses. The highest hardness value of about 45 Gpa was obtained at the Si content of around 7.7 at.%. With increase of Si content, the size of TiN crystallites was reduced and their distribution was changed from aligned to randomly orientated states. Surface roughness of Ti-Si-N film also decreased with increase of Si content.