Temperature and frequency dependence of dielectric and electrical properties was investigated in cerium and manganese doped Sr$\_$0.6/Ba$\_$0.4/Nb$_2$O$\_$6/(60SBN) ceramic system. Structural deformation of 60SBN by dopants did not appeared. 1350$^{circ}C$-10 h sintered specimen had higher densification than 1250$^{circ}C$-10 h sintered one, to which dielectric properties are related. That the feature of dielectric maxima peaks was typical Diffusive Phase Transition (DPT), it was explained by "random-field Ising model". Even though 60SBN has large dielectric loss at high frequency above 100 ㎑, it is desirable for optical applications because of low dielectric loss at low frequency. From Arrhenius plot of temperature, the activation energy was calculated to 0.45∼0.49 eV.