TiO$_2$-WO$_3$(8.2wt%) coatings were prepared by the APS (Atmospheric Plasma Spraying) process to clarify the relationship between the process parameters(H$_2$ gas flow rate of plasma 2nd gas and spraying distance) of the APS coating and photo-decomposition efficiency kinetics of the MB(methylene blue) aqueous solution decomposition and to understand the effect of addition of WO$_3$ on photocatalytic properties of TiO$_2$ sprayed coating. Further, the temperature and velocity of flying particles were measured by DPV-2000 to investigate the relationship between microstructure of coatings and process parameters. Properties of coatins were investigated by XRD, SEM, XPS, RAMAN, UV/VIS spectrometer. In case of the TiO$_2$-WO$_3$(8.2wt%) coating, it had a lower anatase fraction than that of pure-TiO$_2$ coatings because of flying in the higher temperature plasma plume by the heavy weight of TiO$_2$, WO$_3$. And, when WO$_3$ added powders were spayed, the doping effects of W ions substituted into the Ti ion sites was not occured during melting and solidification cycles of spraying. It was found that the addition of WO$_3$ was ineffective effective on increasing photo-decomposition efficiency of TiO$_2$ sprayed coating.