The effect of 0-0.7 ㏖% addition of $Cr_2$$O_3$on the dielectric, pyroelectric, and piezoelectric properties were studied in the (Mg$0.7Pb_{1}$$3/Nb_{2}$3/)$O_3$-$0.3PbTiO_3$(0.7PMN-0.3PT) ceramics with composition near the morphotropic phase boundary. The dielectric constant and loss of the ceramics samples were measured as a function of temperature at various frequencies (0.1-100 KHz). The pyroelectric coefficient was measured by using the Byer-Roundy method as a function of temperature. Dielectric, pyroelectric, and piezoelectric constant achieved the maximum values of 0.4 ㏖% $Cr_2$$O_3$The transition temperature is continuously shifted to lower temperature with an increase of a small amount of $Cr_2$$O_3$