Calcium phosphate was prepared by chemical reaction formula using Oyster shells and $H_3$$PO_4$solutions. After added to 0.1 M∼0.9$ M H_3$$PO_4$ solution for oyster shell, prepared powders were investigated for heating properties and formation phase with heat treatment temperatures. As the results of XRD analysis of heated powders at $500^{circ}C$∼$1200^{circ}C$,$ CaCO_3$ phases were observed at the temperature of below 900 TEX>$^{circ}C$</TEX> and in the condition of 0.1 M∼0.9 M $H_3$$PO_4$ solutions. However, $CaCO_3$, $CaPO_3$(OH) and $Ca_3$($PO_4$)$_2$ phases were appeared at the temperature range between $500∼900^{circ}C$ and in the solution of 0.7 M to 0.9 M $H_3$$PO_4$. $Ca_{ 5}$($PO_4$)$_3$(OH) and CaO phases due to the decarbonation of oyster shells($CaCO_3$) were appeared at above $1000^{circ}C$ and in the solution of below 0.5 M $H_3$X$PO_4$. However in the case of above 0.7 M $H_3$$H_4$ solutions, $Ca_{5}$ ($PO_4$)$_3$(OH) was decomposed into $Ca_3$($PO_4$)$_2$ at more higher 100$0^{circ}C$. Thus $Ca_3$(X$Ca_4$)$_2$ phases were appeared at higher than 100$0^{circ}C$.