The hydrogen redistribution induced by thermotransport at temperatures likely to be encountered in nuclear power reactors (300-$340^{circ}C$) was investigated in modified Zircaloy-4 alloys. Modified Zircaloy-4 alloys were prepared by altering the chemical composition of Zircaloy-4; the oxygen content of Zircaloy-4 (0.1 wt%) was increased to 0.2, 0.5 and 1.0 wt%. The heat of transport ($Q^{*}$ ) for hydrogen was measured by changing the initial hydrogen and oxygen concentrations. It was found that the heat of transport was not affected by increases in the initial hydrogen concentration from 63.3 to 91.7 ppm. However, the value of $Q^{Q}$ decreased from 6.8 to 4.5 ㎉/mol as the initial oxygen concentration was increased from 0.2 to 1.0 wt%.