Crystallographic characteristics and interfacial structures of $Al_2$$O_3$and $ZrO_2$dielectric films prepared by atomic layer chemical vapor deposition (ALCVD) were investigated at atomic scale by high-resolution transmission electron microscopy (HRTEM) and energy dispersive X-ray spectroscopy (EDS)/electron energy-loss spectroscopy (EELS) coupled with a field-emission transmission electron microscope. The results obtained from cross-sectional and plan-view specimens showed that the $Al_2$$O_3$film was crystallized by annealing at a high temperature and its crystal system might be evaluated as either cubic or tetragonal phase. Whereas the $ZrO_2$film crystallized during deposition at a low temperature of ∼$300^{circ}C$ was composed of both tetragonal and monoclinic phase. The interfacial thickness in both films was increased with the increased annealing temperature. Further, the interfacial structures of X$ZrO_2$$O_3$and $ZrO_2$films were discussed through analyses of EDS elemental maps and EELS spectra obtained from the annealed films, respectively.