The corrosion resistance and cytotoxicity behavior of Ti alloys were studied as a function of Nb contents(3wt.%Nb, 20wt.%Nb, 40wt.%Nb). Ti-Nb alloys were melted by vacuum arc furnace and then rolled to 50% reduction ratio after homogenized at 105$0^{circ}C$ for 24hrs. The corrosion resistance of Ti-Nb alloys were investigated by potentiodynamic polarization test in the 0.9% NaCl and 5% HCI solution. Biocompatibility of Ti-Nb alloys was evaluated by cytotoxicity test. The results can be summarized as follows 1) The microstructure change from equiaxial to acicular and the increased $eta$ phase in Ti-Nb alloys were obtained as the Nb content increased. 2) For the corrosion test in the solution of 0.9% NaCl and 5% HCI, the corrosion behavior of Ti-Nb alloys was similar to ASTM grade 2 CP Ti. 3) For the cytotoxicity test, Ti-Nb alloys showed excellent biocompatibility compared to ASTM grade 2 CP Ti, 316L STS and Co-Cr alloys.