The heteroepitaxial growth of crystalline 3C-SiC on 6H-SiC substrates using high purity silane ($SiH_4$) and prophane ($C_3H^8$) was carried out by thermal chemical vapor deposition, and growth characteristics were investigated in this study. In case that the flow ratio of C/Si and flow rate of $H_2$ were 4.0 and 5.0 slm, respectively, the growth rate of epilayers was about 1.8 $mu$m/h at growth temperature of $1200^{circ}C$. The Nomarski surface morphology, X-ray diffraction, Raman spectroscopy, and photoluninescence of grown epilayers were measured to investigate the crystallinity. In this study, the high quality of crystalline 3C-SiC heteropitaxial layers was observed at growth temperature of above $1150^{circ}C$.