Recently, the steel parts used at the aerospace and automobile industries are required to be used light weight parts. Therefore, used material, steel have to be a high stress, which is an indispensable condition in this field. At the consideration of parts design, high hardness of the lightweight parts have an benefit of saving fuel and material. A high stress of metal has a point of difference according to the shape of design, external cyclic load and condition of vibration. A crack generates on the surface of metal or under yield stress by defect of inner metal defect or surface defect and slowly, this crack grow stable growth. Finally, rapidity failure phenomena is happen. Fatigue failure_phenomena, which happen in metal, bring on danger in human life and property therefor, anti-fatigue failure technology take an important part of current industries Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. Therefore, this paper investigated the effect on frcature toughness using shot peening which is improve the resistance of crack growth and crack expansion rate by fatigue that make a compressive residual stress on surface.