We have fabricated a carbon nanotube field emission display (CNT-FED) panel with a 2-inch diagonal size by using a screen printing method and vacuum in-line sealing technology. The sealing temperature of the panel was around 390$^{circ}C$ and the vacuum level was obtained with 1.4x$10^{-5}$torr at the sealing. When the field emission properties of a fabricated and sealed CNT-FED panel were characterized and compared with those of the unsealed panel which was located in a test chamber of vacuum level similar with the sealed panel. As a result, the sealed panel showed similar I-V characteristics with unsealed one and uniform light emission with very high brightness at a current density of 243 ${mu}A/cm^2$, obtained at the electric field of 10 V/${mu}m$.