The dielectric and piezoelectric properties of 0.36Pb($Sc_{1/2}Nb_{1/2}$)$O_{3}$-0.25Pb($Ni_{1/3}Nb_{2/3}$)$O_{3}$-0.39Pb$TiO_{3}$ (hereafter PSNNT) at the morphotropic phase boundary (MPB) composition were investigated with $0{sim}2.5$ mot% $MnO_{2}$ doping. Bulk density, dielectric loss and tetragonality of crystal structure were all improved with increasing $MnO_{2}$ additive content. With increasing $MnO_{2}$ additive content, the electromechanical coupling factor and quality factor were also increased: Electromechanical coupling $k_{p}$ and quality factor $Q_{m}$ at 2.0 mol% $MnO_{2}$ doping with were showed highest values of 55.6 % and 252, respectively.