Pt-doped zinc oxide (ZnO:Pt) films were deposited by ultrasonic spray pyrolysis. Resistivity variation with Pt concentration was measured. The Pt distribution in ZnO:Pt films was studied through Auger Electron Spectroscopy (AES). The ZnO:Pt films were annealed in the ambient of air, water vapor and ozone, respectively. The variation in crystallographic properties and surface morphologies with respect to the annealing condition was observed by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The resistivity variation of the films with the annealing condition was measured. Finally, Atomic Force Microscopy (AFM) measurements were carried out to study the effects of the annealing on the roughness of ZnO:Pt films.