A new method to improve the wet etching characteristics is described. The anisotropic wet-etching of (100) Si with megasonic wave has been studied in KOH solution. Etching characteristics of p-type (100) 6 inch Si have been explored with and without megasonic irradiation. It has been observed that megasonic irradiation improves the characteristics of wet etching such as an etch uniformity and surface roughness. The etching uniformity on the whole wafer with and without megasonic irradiation were less than ${pm}1\%$ and more than $20\%$, respectively. The initial root-mean-square roughness($R_{rms}$) of single crystal silicon is 0.23 nm. It has been reported that the roughnesses with magnetic stirring and ultrasonic agitation were 566 nm and 66 nm, respectively. Comparing with the results, etching with megasonic irradiation achieved the Rrms of 1.7 nm on the surface after the $37{mu}m$ of etching depth. Wet etching of silicon with megasonic irradiation can maintain nearly the original surface roughness after etching process. The results have verified that the megasonic irradiation is an effective way to improve the etching characteristics such as etch uniformity and surface roughness.