In this paper, we analyzed on the characteristics of the stranded wire disconnected by repeated stress. The stranded wires that were used in the experiment are PVC insulated flexible cords(VCTFK: Vinyl Insulated Vinyl Cabtyre Cord Flat-type) of $0.75mm^2,;1.25mm^2,;and;2.0mm^2$. They are used to connect the load in low voltage. The stranded wires disconnected by repeated stress were magnified with optical microscope. Using X-ray, the disconnected wire were photo-graphed. we compared mechanical characteristics of the stranded wire between disconnected tendency and allowable current. On the mechanical strength of vinyl cap tire ellipse type cords under bending stress, VCTFK of $1.25mm^2$ was the strongest of them. When it was bent $826.3pm7$ times, it appeared the disconnected tendency that element wires of VCTFK of $1.25mm^2$ are more about 1.67 times than element wires of VCTFK of $0.75mm^2$. In mechanical strength, VCTFK of $1.25mm^2$ is higher about 1.7 times than VCTFK of $0.75mm^2$. Therefore, we found out that mechanical strength was higher, when the wire had a lot of element wires. In comparison with bending stress, VCTFK of $1.25mm^2$ is the strongest among samples, and it is the most useful in wires of movable type.