From the gradual increasing state of charge (GISOC) observations, electrochemical behavior of multi-walled carbon nanotube│(lM LiP $F_{6}$ , EC,DEC,DME 3:5:5 volume ratio)│lithium cells was evaluated using the galvanostatic charge-discharge process. A MWCNT delivers a specific charge capacity of 1,300 mAh/g in a Li cell when cycled up to an end voltage of 0 V (vs. Li/L $i^{＋}$ )at a constant current rate every 10 hours. However, in the present study, the specific discharge capacity obtained is 338 mAh/g, thus amounting to a coulombic efficiency of only 26％. Further, when the MWCNT│Li cells were tested using the GISOC method, two distinguishable linear-fit ranges were observed due to the intercalation/deintercalation of lithium, which were found to have II $E_1$, IIC $s_1$ and II $E_2$of 27.3％, 372 mAh/g, and 25.5％, respectively. Q $c_1$, could be calculated from the data of IIE and IICs of each range by the modified equation "II $C_{sum}$= $Sigma$( $Q_{C}$- $Q_{D}$)=(II $E_{1}$$^{-1}$ ) $Q_{Dl}$ ＋(II $E_2$$^{-1}$ -1) ( $Q_{D2}$- $Q_{Dl}$ ) ＋ IIC $s_1$= $Q_{Cl}$ - $Q_{Dl}$ ". Results of the GISOC method could be converted to the results of galvanostatic charge-discharge process, irrespective of the state of charge of the cell or battery.ery.y.y.