Tungsten is widely used as a plug for the multi-level interconnection structures. However, due to the poor adhesive properties of tungsten(W) on SiO$_2$ layer, the Ti/TiN barrier layer is usually deposited onto SiO$_2$ for increasing adhesion ability with W film. Generally, for the W-CMP(chemical mechanical polishing) process, the passivation layer on the tungsten surface during CMP plays an important role. In this paper, the effect of oxidant on the polishing selectivity of W/Ti/TiN layer was investigated. The alumina(A1$_2$O$_3$)-based slurry with $H_2O$$_2$ as the oxidizer was used for CMP applications. As an experimental result, for the case of 5 wt％ oxidizer added, the removal rates were improved and polishing selectivity of 1.4:1 was obtained. It was also found that the CMP characteristics of W and Ti metal layer including surface roughness were strongly dependent on the amounts of $H_2O$$_2$ oxidizer.