Crystal structure of $(Ba-{1-x}La_x)[Mg_frac{1+x}{3}}Nb_frac{{2-x}{3}}]O_3$ (BLMN) ceramics with 0leq1x geq was investigated using synchrotron X-ray powder diffraction (XRD) and high reso(B $a_{l-x}$L $a_{x}$)[M $g_{(1+x)}$3/N $b_{(2-x)/3}$］ $O_3$lution transmission electron microscopy (HRTEM). When the La content, x, is above 0.1, the 1:2 ordered hexagonal structure found in Ba($Mg_frac{1}{3}Nb_frac{2}{3}})O_3$(BMN) was transformed into 1:1 ordered cubic structure. The 1:1 ordered cubic structure was maintained up to x=0.7. When x exceeded 0.7, however, BLMN was transformed into 1:1 ordered structure which has cation displacement and in-phase and anti-phase tilt of octahedra.dra.