The $ZnNb_2O_{6}$ ceramics with CuO(1, 3, 5wt%) were prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of $950^{circ}C$∼$1075^{circ}C$ for 3hr in air The structural properties and the microwave dielectric properties of $ZnNb_2O_{6}$ ceramics were investigated with sintering temperature and the addition of CuO. Increasing the addition of CuO, the peak of second phase($Cu_3Nb_2O_{8}$) was increased. The grain size of the $ZnNb_2O_{6}$ ceramics with CuO was increased with CuO addition at same temperature. The dielectric constant of $ZnNb_2O_{6}$ ceramics with CuO was increased with sintering temperature and CuO addition. While the quality factor of the $ZnNb_2O_{6}$ ceramics with lwt% CuO depended on sinterability, the quality factor of $ZnNb_2O_{6}$ with 3wt% and 5wt% CuO depended on second Phase due to the CuO addition. The optimum dielectric Properties of $varepsilon$$_{r}$ = 21.73 Q${ imes}$f = 19,276 were obtained from the condition of 3wt% CuO addition and sintering temperature of $1025^{circ}C$(3hr).