High-temperature Superconductor(HTS) tubes were fabricated in terms of different chemical compositions and various SrSO$_4$additions by centrifugal forming method. For powder melting by induction the optimum range of melting temperatures and preheating temperature were 1050$^{circ}C$, 1100$^{circ}C$ and 550$^{circ}C$ for 30 min, respectively. The mould rotating speed was 1000 rpm. A tube was annealed at 840$^{circ}C$ for 72 hours in oxygen atmosphere. The plates like grains more than 20 $mu extrm{m}$ were well developed along the rotating direction of mould regardless of initial chemical compositions and the amounts of SrSO$_4$in Bi2212. The specimen with Bi2212 composition exhibited T$\_$c/ of 83 K, while the specimens fabricated with other compositions are lower than 60 K. The measured I$\_$c/ and J$\_$c/ at 77 K(B = 0 T) in Bi2212 with 7 % SrSO$_4$ composition were about 680 A and 380 A/$ extrm{cm}^2$.