This study discussed the dyeing of wool and cotton fabrics with Betel Palm Tree White woolen fabrics and cotton fabrics purchased from HATH (Korea Apparel Testing ＆ Research Institute) were used as experimental fabrics. Using dyeing powder extracted from dyeing material, various temperatures, dyeing times, and pH were used in the dyeing process. Al, Cr, Fe, Cu, and Sn were used as mordant and the absorption was compared with different mordanting methods. The optimum condition for pre-mordanting dyeing was dye concentration of 25% (o.w.f) and mordant concentration of 0.5$^{circ}$∼1%. Woolen fabric showed an increase of absorption and the maximum absorption was achieved at weak acidity. According to the mordanting methods, woolen fabrics and cotton fabrics were treated with various mordanting agents, a mordant rate of 1:100, at 60$^{circ}C$, for 30 minutes and dyed with a dyeing material concentration of 25% (o.w.f), at a rate of 1:100, at 60$^{circ}C$ for 60 minutes. The best dyeing effect w3s achieved at the temperature of 60$^{circ}C$ for cotton and 80$^{circ}C$ for wool fabrics. The light fastness of cotton and wool fabrics was low and particularly the fastness to perspiration was decreased with Fe mordanting. I concluded that pre-mordanting method was better than post-mordanting method for cotton and woolen fabrics.