In recent, development of nano fiber has been one of the most active subjects in the world. Nano fiber is defined as a ultra fine yarn with a diameter unit of $10-100 imes10^{-9}meter$, which is possible to be produced by an electro-spinning technology. In this study, physical characteristics and dyeing properties of nylon 66 nano fiber were investigated. Nylon 66 nano fiber was dyed with levelling type acid dyes. X-ray diffraction method and DSC analysis were used for the measurement of the degree of crystallization. Analysis of amino end groups was also performed in order to examine a relationship between number of amino groups and its dyeing property as well as water absorption behavior. The maximum exhaustion % of dyes and dyeing rate under various dyeing conditions, such as dyeing temperature and pH in dye bath, along with build-up properties for 2 acid dyes were evaluated. It was found that the degree of crystallization of nano fiber was smaller than that of regular fiber, and amino end groups of nano fiber were less than regular fiber. Half dyeing time of nano fiber was shorter than regular fiber because of the bigger specific surface area. Effect of pH on exhaustion % was small in case of nano fiber. Exhaustion of nano fiber increased with higher concentration of dye.