In this study, the surface properties of PET film were analyzed after plasma surface treatment. After plasma treatment of surface roughness and XPS were evaluated to analyze the chemical property, while the surface potential decay and surface resistance rate was measured to analyze the electric관 characteristic. When plasma discharge treatment was conducted for less than 10 minutes, the electrical insulating property was improved by evaporation of low molecular weight materials and cleaning of surface. However, when the treatment was conducted for more than 10 minutes, the insulating property was decreased due to excessive discharge energy. Analyses of chemical characteristics showed that 10-minute treatment resulted in increase of C-O and O=C-O bonds. However, when treated for more than 10 minutes. they were relatively decreased.