The samples were prepared with hydroxyapatite(HAp) powder and eugenol (Eugenol/HAp = 15, 20, 25, 30wt%). The samples were dried at room temperature. The higher mechanical properties was observed in HAp sample with 25wt% Eugenol. The average compressive and bending strength in HAp with 25wt% Eugenol are 542 kgf/$ extrm{mm}^2$ and 366 kgf/$ extrm{mm}^2$ respectively. This strength is higher compare to that of the cortical bone.