Micro-Pulling Down (${mu}$-PD) 법을 이용하여 $MnO_2$와 $Tb_4O_7$를 첨가하여 crack. 열 strain 등의 결함이 없는 화학양론조성의 $LiNbO_3$ 단결정을 c-축으로 직경 1.0mm, 길이 25-30mm의 크기로 성장시켰다. Electron Probe Micro Analysis (EPMA)를 이용하여 결정 내에 $MnO_2$와 $Tb_4O_7$이 균일하게 분포되어 있음을 확인하였다. 또한 Fourier Transform-Infrared Spectrophotometer (FT-IR)을 사용하여 OH 흡수밴드를 관찰하였고, 성장된 결정의 $MnO_2$와 $Tb_4O_7$ 첨가에 따른 형광특성의 변화를 측정하였다.
Using the Micro-Pulling Down (${mu}$-PD), $MnO_2$ and $Tb_4O_7$ co-doped crack-free stoichiometric $LiNbO_3$ single crystals were grown in 1.0 mm diameter and 25-30 mm length for c-axis. The homogeneous distributions of $MnO_2$ and $Tb_4O_7$ concentration were confirmed by the Electron Probe Microanalysis (EPMA). Also, the infrared OH absorption band of the single crystals observed by using a Fourier Transform-Infrared Spectrophotometer (FT-IR) at room temperature and the photoluminescence spectra was measured with respect to the $MnO_2$ and $Tb_4O_7$ doping.