To investigate the characteristics of phases formed in iron carbides, super iron carbide was synthesized from hematite fines with $CO-H_2$ gas mixture after reduction under $H_2$ gas at $600^{circ}C$. Before carburization, the surface of iron powder reduced was pre-treated in the atmosphere of 0.05 vol% $NH_3$-Ar. The synthesized iron carbides were comprehensively explored by C/S analyzer(Low C/S determinator), M$"{o}$ssbauer spectroscopy, X-ray diffraction patterns(XRD), scanning electron microscopy(SEM), transmission electron microscopy(TEM), and Raman spectroscopy at various reaction time of 5, 10, 15, 20, 25, 30, and 35 min, respectively. By adding a small amount of $NH_3$ gas, the super iron carbides containing 10 wt% carbon were synthesized, and its addition stabilized iron carbides. It was found that the $NH_3$ treatment played a major role in the formation of iron carbide without decomposition($Fe_3C{ o}$3Fe+C) of iron carbides and precipitation of free carbon. It also succeed to synthesize super iron carbide, $Fe_5C_2$, as a stable single phase without involving Fe and $Fe_3C$ phases.