Three-dimensionally ordered macroporous (3DOM) structures of the $LiCoO_2$ electrode materials for Li secondary batteries were fabricated by using the close-packed arrays of PMMA spheres served as templates. In order to successfully fabricate the cathode materials with highly ordered array form, the metal citrates were applied to new precursors. The precursor/template composites were prepared by the infiltration with metal citrate precursors into the voids of template. By removing the PMMA templates, then, the inverse opal structures with the uniform pores of narrow size distribution were resulted. It was confirmed that the 3DOM $LiCoO_2$ material is to take a single phase of rocksalt (R3m) structure. In addition, 3DOM $LiNiO_2$ and $LiMn_{2}O_4$ cathode materials were fabricated using an identical preparation procedure. Also, the morphology of the 3DOM cathode materials calcined at $500^{circ}C;to;700^{circ}C$ was observed by scanning electron microscope.