This article describes the change of hand value of chitosan crosslinked cotton fabrics. The chitosan crosslinked cotton fabrics were manufactured by mercerizing process using epichlorohydrin(ECH) as crosslinkins agent, 2% aqueous acetic acid as a solvent of chitosan and ECH, and 20% aqueous sodium hydroxide as a mercerizing agent and crosslinking catalyst. Cotton fabrics were dipped in the mixed solution of chitosan and ECH, picked up by mangle, mercerized and crosslinked in NaOH solution, and finally wash and dry. Mechanical and physical properties of the chitosan crosslinked fabric were investigated using Kawabata Evaluation System(KES) and other instruments. Tensile energy and tensile strain were decreased with the increase of the concentration of chitosan. Tensile resilience, compression resilience bending rigidity, bending hysteresis, shear stiffness, shear hysteresis, coefficient of friction, geometrical roughness, compression linearity, compressional energy, and thickness were increased with the increase of the concentration of chitosan. On the other hand, bending rigidity, bending hysteresis, coefficient of friction, geometrical roughness, compressional resilience, and thickness were increased with the increase of the concentration of crosslinking agent(epichlorohydrin).