To study the lipid adsorption characteristic of chitosans with different molecular weights and the degrees of deacetylation, in vitro test and near-infrared (NIR) spectroscopic analysis have been performed for the measurement of lipid adsorption characteristics of chitosan. The degrees of deacetylation in chitosans were $70{\%},;85{\%};and;92{\%}$ at different deacetylation times (1 hr, 2 hrs, 3 hrs), respectively. The molecular weight of each chitosan was controlled by enzymatic hydrolysis, and then the molecular weight of the chitosan was 4 kDa. The bulk density, water holding capacity and fat binding capacity of each chitosan powder were $96.2-504.0{\%},;374.4-1217.9{\%},;and;307.0-659.3{\%}$, respectively. The higher molecular weight of chitosan was exhibited the lower bulk density and the higher water and fat binding capacities. Bindinf capacities of chitosan powders to bile salts, cholesterol and linoleic acid were $41.2-63.3{\%},;40.8-67.4{\%},;42.6-72.6{\%}$, respectively. In NIR spectrum of lipid adsorbed chitosan the occurrence static eletronical binding between chitosan and lipid was identified by NIR spectrum peak induced from combination of carboxylic group in lipid and amino group in chitosan. In conclusion, the higher degree of deacetylation and molecular weight of chitosan showed the higher lipid binding capacity and the lipid adsorption of chitosan were occurred by combination of carboxylic group in lipids and amino group in chitosan.