In the present study, a simple method was successfully used for hydroxyapatite coatings on Ti-6Al-4V substrates deposited by using a sol-gel derived precursor. Prior to hydroxyapatite coating the samples were micropolished (0.1 micron) and divided into three sets. The first set,were the micropolished samples kept as such. The second set were coated with titania sol and the third set was treated with 5M NaOH. After three repetitions of hydroxyapatite coating procedures on each set and heat treatment at 600 $^{circ}Delta C$, the formation of hydroxyapatite has been confirmed by XRD analyses and the substrate material was found to be oxidized with negligible amount of CaO in the coating. The SEM studies revealed surface morphology. Hydroxyapatite, calcined at 600$^{circ}Delta C$, displaying a porous structure arisen from heating of the bulk. But, it is very meaningful in trying to approach morale management plans with an object of dental technicians. It is necessary that dental technicians should make efforts to control themselves.