Room and high temperature deformation behaviors of Cu-Zr-Ti-Pd bulk metallic glasses produced by copper mold casting were investigated. The addition of Pd was shown to enhance the glass forming ability and thermal stability of Cu-Zr-Ti base bulk metallic glass. The compressive strength of $Cu_{55}Zr_{30}Ti_{10}Pd_5$ bulk metallic glass was 2230 MPa with 1.8 plastic strain. The stress overshoot and yield drop phenomenon were observed below $487^{circ}C$ and a drastic decrease in the flow stress was observed at $487^{circ}C$. The stress overshoot is thought to be associated with stress-induced structural relaxation.