The hydrogen sorption properties of $Ti_{0.3}Zr_{0.2}V_{0.5}$ NEC(non-evaporable getter) alloy and its hydrides were evaluated at room temperature. The alloy and hydride powders were prepared by the Hydride-DeHydride(HDH) method. The hydrogen sorption speed of $Ti_{0.3}Zr_{0.2}V_{0.5}$ alloy was measured to increase with the amounts of hydride phase in the getter. The hydrogen sorption speeds of $Ti_{0.3}Zr_{0.2}V_{0.5},;(Ti_{0.3}Zr_{0.2}V_{0.5})H_{1.52},;and;(Ti_{0.3}Zr_{0.2}V_{0.5})H_{1.94}$ were 2.22, 3.14 and 5.08 liter/sec, respectively. The unexpected enhancement of hydrogen sorption speed with the presence of the hydride phase is considered to be due to the pre-saturation of hydrogen trap sites which can retard the diffusion of hydrogen in the alloy.