Chitosan is the affinitive finishing agent and gives susceptible effect in textile finishing. In order to examine the modification of polyester fabric treated with chitosan, we observed the characteristic of polyester fabric surface and measured its physical properties. For the purpose of confirming the adhesion of cationic material, we made a comparative study on anionic acid dye. The fabric was treated with crosslinking agent after chitosan finishing. Glutardialdehyde as crosslinking agent was used to improve the fixation rate of chitosan on the polyester fabric. And the US value was increased according to increasing of chitosan concentration. As the concentration of crosslinking agent was increased, whiteness index of the fabric chitosan treated was increased. Moisture regain of the fabric treated with $1\%$ chitosan was doubled and that treated with $2\%$ chitosan was tripled comparing with original fabric. Tensile strength of the chitosan treated fabric had been an increase of $10\%$ compared with alkali treated fabric and crease resistance decreased regardless of chitosan concentration.