The structural and microwave dielectric properties of $0.7Mg_4Ta_2O_9-0.3SrTiO_3$ ceramics with sintering temperature were investigated. All the sample of the $0.7Mg_4Ta_2O_9-0.3SrTiO_3$ ceramics were prepared by conventional miked oxide method and the sintering temperature was $1425~1500^{circ}C$. The hexagonal phase of $Mg_4Ta_2O_9$ and the cubic phase of $SrTiO_3$ were coexisted. The porosity of $0.7Mg_4Ta_2O_9-0.3SrTiO_3$ ceramics were reduced with increasing sintering temperature. In the case of $0.7Mg_4Ta_2O_9-0.3SrTiO_3$ ceramics sintered at $1475^{circ}C$, dielectric constant, quality factor and temperature coefficient of resonant frequency were 14.51, 82,596 GHz and $-3.14;ppm/^{circ}C$, respectively.