Generally, the strength achieved of glass-ceramics is higher as is the fracture toughness, as compared with the original glass. This improvement is due to the microstructure consisting of very small crystals. In this study, Ag-doped $45SiO_2-24CaO-24Na_2O-4P_2O_5$ glasses were irradiated to strengthen by the crystallization using Femto second laser Pulses. Through the UV/VIS spectroscope, XRD, Nano-indenter and SEM etc., heat-treated and irradiation of laser pulses without heat-treated samples were analyzed. Two kinds of samples, heat-treated and laser irradiated without heat-treated samples, showed the peaks in the same wavelength near 360 nm. Especially, samples irradiated by 140 mW laser with XYZ stage having at the rate of 100$~$l000 $mu$m/s had the largest absorption peak among them, and heat-treated samples was shown lower absorption range than over 90 mW laser irradiated samples. Moreover, samples irradiated by laser had higher values ($4.4~4.56{ imes}10^{-3}(Pa)$) of elastic modulus which related with strength of glass than values of heat-treated samples and these are 1.2$~$1 .5 times higher values than them of mother glass.