Fracture behavior was investigated in the $Al_2O_3-TiO_2(3 wt{\%})-LaPO_4(25 wt{\%}$) composite ceramics. To improve the fracture toughness of alumina ceramics, $TiO_2$ and $LaPO_4$ as a second phase were introduced. The samples were made by conventional powder processing method. Green compacts were sintered at $1600^{circ}C$ for 2 h in air. Fracture toughness was tested using Indentation Strength Bending(ISB) method. From the bending test, enhanced fracture toughness was found in the composite, compared to the pure and $TiO_2$-doped alumina. The main factor of the enhancement of fracture toughness seems to be attributed to the weak interphase role of the $LaPO_4$ as a particulate type.