Aluminum alloy casting is gaining increased acceptance in automotive and electronic industries and especially, squeeze casting is the most efficient method of mass manufacturing of such parts. In this study, the microstructures and mechanical properties of Al-7.0Si-0.4Mg(AC4C) alloy fabricated by squeeze casting process for development of fuel system parts (fuel rail) are investigated. The microstructure of squeeze cast specimen was composed of eutectic structure aluminum solid solution and $Mg_2Si$ precipitates. The tensile strength of as-solid solution treatment Al-7.0Si-0.4Mg alloy was 298.5MPa. It was found that Al-7.0Si-0.4Mg alloy had good corrosion resistance in electrochemical polarization test.