In this research, silicone rubber with additions of inorganic filler, alumina trihydrate$(Al(OH)_3;:;ATH)$, was aged acceleratedly and cyclically by the salt-fog and heating. The optimum amount of ATH addition to silicone rubber have been investigated by measurements of leakage current in the change of electrical properties and tensile strength, %elongation in mechanical properties and FT-IR, TG, SEM in the change of the chemical properties. With regard to un-aged silicone rubber, as the ATH addition amount increases, conductive path formation time was shortened in the electrical properties and tensile strength was increased, %elongation was decreased. In case of identical ATH addition amount, as cyclic aging increases, surface resistivity, tensile strength and %elongation were decreased. Considering the cyclic aging, the most effective amount of ATH addition was about 90phr.