This study was carried out for effective utilization of recycling resources to investigate the repulping conditions of car air filter waste paper and to evaluate the application into corrugating medium papermaking by blending these repulped pulps. Car air filter waste paper was made of virgin BKP and it was dipped into phenol resin solution. It was well disintegrated by laboratory Valley beater with 10%(basis on oven-dried pulp weight) NaOH addition and defoamer usage. The optimal temperature, beating consistency and treatment time were mainly $40^{circ}C$, 1% and $30{sim}40$ minutes, respectively. Handsheets were prepared with various blending ratios between air filter recycled pulp and KOCC. In the case of $10{sim}20%$ substitution with air filter recycled pulp, physical properties reductions as compressive strength and burst strength of sheets were lower than others. These results showed more favour than the partial substitution of KOCC for corrugating medium even though some strength reduction of paper. It was also observed that the waste water of air filter recycling was not affective to environmental problems.