Four kinds of new aliphatic diols were synthesized by the ring opening reaction of glycolide with 1,4-butanediol, 1,6-hexanediol, 1,4-cyclohexanediol, or 1,4-cyclohexanedimethanol, a difunctional initiator, in the presence of stannous octoate catalyst. The resulting diols were melt-polymerized with succinic acid, adipic acid, or suberic acid at 170, 190, or $220^{circ}C$ to produce new sequentially ordered aliphatic polyesters and their corresponding polyesters with random structure. Their glass transition temperatures ($T_g$) ranged from -40 to $30^{circ}C$, The sequentially ordered polyesters prepared at $170^{cir}C$ had higher $T_g$ of 5 to $10^{circ}$ than the polyesters with rand()m structure produced at higher temperature. From in-vitro degradation test the sequentially ordered polyesters was shower in the rate of hydrolysis in a buffer solution than the polymers with random molecular structure