This paper was investigated the changes of surface properties of high-temperature-vulcanized (HTV) semiconductive silicone rubber due to oxygen plasma discharge. The modifications produced on the silicone rubber surface by oxygen plasma were accessed using Fourier transform infrared spectroscopy(FTIR), X-ray photoelectron spectroscopy(XPS), contact angle and Surface Roughness Tester. The results of the chemical analysis Showed that C-H bonds were broken due to plasma discharge and Silica-like bonds (SiOx, x=$3~4$) increased. It is thought that the above changes lead to the increase of surface energy of high-temperature-vulcanized (HTV) semiconductive silicone rubber also, Surface roughness was increased with cleavage of side-chains and oxidation process, it confirmed change as the SEM. The micromorphology of surface and hydrophobicity due to plasma discharge based on our results were discussed.