[ $(Y_{0.5}Sm_{0.25}Nd_{0.25})Ba_2Cu_3O_y$ ] [(YSN)-123] high $T_c$ composite superconductors with $CeO_2$ addition were systematically investigated by top seeded melt growth (TSMG) process in air atmosphere. A melt textured $NdBa_2Cu_3O_y$ (Nd-123) single crystal was used as a seed for achieving the c-axis alignment large grains perpendicular to the surface of (YSN)-123 composite oxides. The size of $(Y_{0.5}Sm_{0.25}Nd_{0.25})_2BaCuO_5$ [(YSN)211] nonsuperconducting inclusions of the melt textured (YSN)-123 samples with $CeO_2$ addition were remarkably reduced and uniformly distributed within the (YSN)123 superconducting matrix except in the region very close to the Nd-123 seed crystal. The sample showed a sharp superconducting transition of 91 K.