A new $MoO_3$ based microsensor with low power consumption was presented. Typical size of sensor was 5mm in width and 8mm in length. As a sensitive electrode, $MoO_3$ was successfully fabricated by IC technology on pyrex glass of $250{mu}m$ in thickness. After annealing at $550^{circ}C$ for 3hrs, the film was fully crystallized and demonstrated as pure $MoO_3$ structure. The grain size of $MoO_3$ was plat like and typical size was about $1{mu}m$. Based on the results of sensitivity measurement, $MoO_3$ microsensor shows especially high selectivity to $H_2$ reducing gas atmosphere. The applied heater power was lower than 0.5 Watt.