Fatigue life and notch sensitivity of the ultrafine grained pure Ti produced by ECAP was investigated. The ECAPed sample with the true strain of 460$\%$ showed near equiaxed grains with an average size of about 0.3 $mu$m. After ECAP, the ultimate tensile strength was increased by 60$\%$, while the tensile ductility was decreased by 31$\%$. The ECAPed ultrafine grained pure Ti samples showed high notch sensitivity and significant improvement of high cycle fatigue limit by a factor of 1.67. The ECAPed samples also show high notch sensitivity (K$_{f}$/K$_{t}$ = 0.96). It can be concluded that ECAP is the effective process for achieving high fatigue strength in Ti by increasing its tensile strength through grain refinement