The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated by the screen printing method on alumina substrates. The effect of the sintering temperature on the microstructure and dielectric properties of the $BaTiO_3/SrTiO_3$ thick films has been investigated. The relative dielectric constant and dielectric loss at 1 MHz of the $BaTiO_3/SrTiO_3$ heterolayered thick films with sintering temperature of $1350^{circ}C$ were about 751 and 1.74, respectively. The remanent polarization $(P_r)$ of the pure $(Ba_{0.5}Sr_{0.5})TiO_3$ and $BaTiO_3/SrTiO_3$ heterolayered films are approximately $5.1;{mu}C/cm^2$ and $10;{mu}C/cm^2$. This study suggests that the design of the $BaTiO_3/SrTiO_3$ heterolayered thick films capacitor with different phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.