We have studied the Ge redistribution after dry oxidation and the oxide growth rate of $Si_{1-x}Ge_x$ epitaxial layer. Oxidation were performed at 700, 800, 900, and $1,000;^{circ}C$. After the oxidation, the results of RBS (Rutherford Back Scattering) & AES(Auger Electron Spectroscopy) showed that Ge was completely rejected out of the oxide and pile up at $Si_{1-x}Ge_x$ interface. It is shown that the presence of Ge at the $Si_{1-x}Ge_x$ interface changes the dry oxidation rate. The dry oxidation rate was equal to that of pure Si regardless of Ge mole fraction at 700 and 800$^{circ}C$, while it was decreased at both 900 and $1,000^{circ}C$ as the Ge mole fraction was increased. The dry of idation rates were reduced for heavy Ge concentration, and large oxiidation time. In the parabolic growth region of $Si_{1-x}Ge_x$ oxidation, the parabolic rate constant are decreased due to the presence of Ge-rich layer. After the longer oxidation at the $1,000^{circ}C$, AES showed that Ge peak distribution at the $Si_{1-x}Ge_x$ interface reduced by interdiffusion of silicon and germanium.