[$TiO_2$] sol and $SiO_2$ sol were prepared using sol-gel method. As $H_{2}O$/Alkoxide ratios increased, sol had cluster structure and as $H_{2}O$/Alkoxide ratios decreased, sol had linear structure. Gelation time of $TiO_2$ sol was faster than that of $SiO_2$ sol according to the time. In comparison with initial viscosity between $TiO_2$ sol and $SiO_2$ sol, $TiO_2$ sol was highest at $H_{2}O/Ti(OC_{3}H_{7})_{4}=5$, $SiO_2$ sol was almost constant according to $H_{2}O/Si(OC_{2}H_{5})_{4}$ ratios.