Directionally melt-textured high $T_c;(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_{2}Cu_{3}O_y$ [(YNS)-123] superconductor was systematically investigated by the zone melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{2}BaCuO_5$[(YNS)211] inclusions were uniformly dispersed in large $(Y_{0.5}Nd_{0.25}Sm_{0.25})Ba_{2}Cu_{3}O_y$ [(YNS)123] matrix. High irreversibility field and magnetization hysteresis loop of the zone melt-textured (YNS)-123 sample exhibited the enhanced flux pinning, compared with $YBa_{2}Cu_{3}O_y$ (Y-123) sample without RE(rare earth). Critical current density of (YNS)-123 sample was $2.5{ imes}10^4;A/cm^2$ at 2 T and 77 K.